Corrosion behavior of UNS S31803 steel with changes in the volume fraction of ferrite and the presence of chromium nitride.
Nenhuma Miniatura disponível
Data
2015
Título da Revista
ISSN da Revista
Título de Volume
Editor
Resumo
The goal of this study was to examine the changes caused in stress corrosion cracking and the critical pitting temperature behavior of a UNSS31803 duplex stain less steel due to variations in the ferrite fraction and the presence of chromium nitride in their microstructure. The steel plates were cold rolled and annealed at 1060 °C. Microstructural variations in the plates were produced by thermal annealing treatments a t1200 °C and 1300 °C. Steel annealed at 1060 °C showed greater resistance to stress corrosion cracking than steel annealed at 1300 °C. Steel annealed at 1300 °C had the lowest critical pitting temperature.
Descrição
Palavras-chave
Stainless steel, Polarization, Pitting corrosion, Stress corrosion cracking
Citação
LACERDA, J. C. de; CÂNDIDO, L. C.; GODEFROID, L. B. Corrosion behavior of UNS S31803 steel with changes in the volume fraction of ferrite and the presence of chromium nitride. Materials Science & Engineering. A, Structural Materials: Properties, Microstructure and Processing, p. 428-435, 2015. Disponível em: <http://www.sciencedirect.com/science/article/pii/S0921509315304305>. Acesso em: 11 jul. 2016.