Title: | Evaluation of hydrogen-Induced cracking resistance of the In625 laser coating system on a C-Mn steel substrate. |
Authors: | Trindade, Vicente Braz Almeida, Natália Chaves Cândido, Luiz Cláudio Faria, Geraldo Lúcio de Lima, Milton Sérgio Fernandes de |
Keywords: | Laser cladding Pitting |
Issue Date: | 2017 |
Citation: | TRINDADE, V. B. et al. Evaluation of hydrogen-Induced cracking resistance of the In625 laser coating system on a C-Mn steel substrate. Evaluation of hydrogen-Induced cracking resistance of the In625 laser coating system on a C-Mn steel substrate. International Engineering Journal, v. 70, p. 181-186, 2017. Disponível em: <http://www.scielo.br/scielo.php?script=sci_arttext&pid=S2448-167X2017000200181>. Acesso em: 29 set. 2017. |
Abstract: | The corrosion of C-Mn steels in the presence of hydrogen sulfide (H2S) represents a significant challenge to oil production and natural gas treatment facilities. The failure mechanism induced by hydrogen-induced cracking (HIC) in a Inconel 625 coating / C-Mn steel has not been extensively investigated in the past. In the present work, an API 5CT steel was coated with In625 alloy using laser cladding and the HIC resistance of different regions, such as the coating surface, the substrate and HAZ, were evaluated. SEM observations illustrated that all HIC cracks were formed at the hard HAZ after 96h of exposure. No HIC cracks were observed in the substrate and the In625 coating after the same exposure duration. Pitting was recorded in the substrate caused by non-metallic inclusion dissolving. |
URI: | http://www.repositorio.ufop.br/handle/123456789/9192 |
metadata.dc.identifier.doi: | https://doi.org/10.1590/0370-44672016700088 |
ISSN: | 1807-0353 |
metadata.dc.rights.license: | A REM - International Engineering Journal - autoriza o depósito de cópia de artigos dos professores e alunos da UFOP no Repositório Institucional da UFOP. Licença concedida mediante preenchimento de formulário online em 12 set. 2013. |
Appears in Collections: | DEMET - Artigos publicados em periódicos |
Files in This Item:
File | Description | Size | Format | |
---|---|---|---|---|
ARTIGO_EvaluationHydrogenInduced.pdf | 1,97 MB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.