Title: Influência do fator de forma e do teor de adição de microfibras de resíduo de lã de vidro na resistência de argamassas de cimento Portland.
Authors: Ferreira, Matheus Henrique Dela Costa
metadata.dc.contributor.advisor: Silva, Guilherme Jorge Brigolini
Silva, Keoma Defáveri do Carmo e
Keywords: Resíduos de vidro - lã de vidro
Sustentabilidade
Cimento
Issue Date: 2023
metadata.dc.contributor.referee: Silva, Guilherme Jorge Brigolini
Aguilar, Maria Teresa Paulino de
Silva, Keoma Defáveri do Carmo e
Citation: FERREIRA, Matheus Henrique Dela Costa. Influência do fator de forma e do teor de adição de microfibras de resíduo de lã de vidro na resistência de argamassas de cimento Portland. 2023. 58 f. Dissertação (Mestrado em Engenharia Civil) - Escola de Minas, Universidade Federal de Ouro Preto, Ouro Preto, 2022.
Abstract: Como se já não bastasse os impactos climáticos causados pela acumulação dos gases estufas na atmosfera, também deve-se enfatizar o problema de contaminação terrestre, devido à adoção de práticas insustentáveis de descarte dos resíduos sólidos. Entre estes resíduos, destaca-se o resíduo de lã de vidro (RLV), oriundo de um tipo de isolamento termoacústico empregado em equipamentos industriais ou em construções residenciais. Neste trabalho, buscou-se uma alternativa para o reaproveitamento do RLV gerado em plantas siderúrgicas como uma fonte de microfibras para adição em matrizes de argamassa de cimento Portland. Dessa forma, foi feita a caracterização química, física e mineralógica do RLV utilizando técnicas de fluorescência e difração de raios-x, e microscopia eletrônica de varredura. Também foram avaliados os impactos na resistência mecânica das matrizes causados tanto pela variação do fator de forma das microfibras, como pelo teor de adição de RLV. Os teores de fibras adicionados nas dosagens propostas para este estudo foram de 0%; 2,5%; 5,0%; 7,5% e 15%. As argamassas com adição de fibras curtas e longas foram ensaiadas para obter a resistência à tração na flexão e à compressão, aos 7 e 28 dias de hidratação em regime submerso a temperatura ambiente. Os resultados das análises estatísticas feitas nos dados de resistência medidos revelaram que as fibras longas, com fator de forma maior, foram mais eficientes no ganho de resistência quando submetidas aos esforços de tração do ensaio de flexão. Já nos ensaios de compressão uniaxial, os efeitos predominantes no ganho de resistência foram promovidos devido a adição das fibras curtas, com menor fator de forma, mas com elevada área de superfície específica, o que favoreceu a formação de uma matriz densa. Portanto, concluiu- se que tanto o teor de adição de fibras quanto o fator de forma tiveram impacto positivo na resistência última. Assim, enquanto a adição de fibras curtas promoveu um ganho máximo de resistência a compressão de 43% para o traço LVM-15, a adição de fibras longas também foi responsável por um incremento máximo de 48% na resistência a tração para o traço LVL-15.
metadata.dc.description.abstracten: As if the climate impacts caused by the accumulation of greenhouse gases in the atmosphere were not enough, the problem of terrestrial contamination must also be emphasized, due to the adoption of unsustainable solid waste disposal practices. Among these wastes, glass wool waste (GWW) stands out, coming from a type of thermoacoustic insulation used in industrial equipment or residential buildings. In this work, an alternative was sought for reusing GWW generated in steel plants as a source of microfibers for addition in Portland cement mortar matrices. Thus, the chemical, physical and mineralogical characterization of the GWW was carried out using x-ray fluorescence and diffraction techniques and scanning electron microscopy. The impacts on the mechanical strength of the matrices caused both by variation of the aspect ratio morphological parameter of the microfibers and by the amount of GWW addition were also evaluated. The levels of fibers added in the dosages proposed for this study were 0%, 2.5%, 5.0%, 7.5%, and 15%. The mortars with short and long fiber content added were tested to obtain the tensile strength in bending and compression strength, at 7 and 28 days of hydration in submerged regime at room temperature. The results of statistical analyses performed on the measured resistance data reveal that the long fibers, with a higher aspect ratio, were more efficient in gaining resistance when subjected to the tensile stresses of the bending test. In the uniaxial compression tests, the predominant effects in the resistance gain were promoted due to the addition of short fibers with a lower aspect ratio but with a larger specific surface area, which favored the formation of a denser matrix. Therefore, it was concluded that the fiber content and aspect ratio positively impacted the ultimate strength. Thus, whereas the addition of short fibers promoted a maximum gain in compressive strength of 43% for the LVM-15 mix, the addition of long fibers was also responsible for a maximum increase of 48% in tensile strength for the LVL-15 mix.
Description: Programa de Pós-Graduação em Engenharia Civil. Departamento de Engenharia Civil, Escola de Minas, Universidade Federal de Ouro Preto.
URI: http://www.repositorio.ufop.br/jspui/handle/123456789/16316
metadata.dc.rights.license: Autorização concedida ao Repositório Institucional da UFOP pelo(a) autor(a) em 28/02/2023 com as seguintes condições: disponível sob Licença Creative Commons 4.0 que permite copiar, distribuir e transmitir o trabalho, desde que sejam citados o autor e o licenciante. Não permite o uso para fins comerciais nem a adaptação.
Appears in Collections:PROPEC - Mestrado (Dissertações)

Files in This Item:
File Description SizeFormat 
DISSERTAÇÃO_InfluênciaFatorForma.pdf4,56 MBAdobe PDFView/Open


This item is licensed under a Creative Commons License Creative Commons