Título: | Secondary recrystallization characteristics of 3%Si grain-oriented electrical steel. |
Autor(es): | Cardoso, Afonso Vaz de Mello Paolinelli, Sebastião da Costa Silveira, Carolina Cesconetto Cota, André Barros |
Palavras-chave: | Grain-oriented steel Magnetic properties |
Data do documento: | 2018 |
Referência: | CARDOSO, A. F. de M. et al. Secondary recrystallization characteristics of 3%Si grain-oriented electrical steel. Journal of Materials Research and Technology - JMR&T, v. 8, n. 1, p. 240-245, jan./mar. 2018. Disponível em: <https://www.sciencedirect.com/science/article/pii/S2238785417301990>. Acesso em: 19 mar. 2019. |
Resumo: | A secondary recrystallization Lab study focusing on the secondary recrystallization temper- ature and magnetic properties was carried out on cold rolling industrial samples of 3%Si grain-oriented electrical steel produced by low slab reheating temperature technology. The results showed a secondary recrystallization temperature, determined by the observed grain size change, of 1080 ◦C with annealing interruption and of 1060 ◦C in annealing for 50 h at constant temperature. In addition, the best set of magnetic properties, the higher induction and the lower core loss values, was achieved by annealing the samples during 50 h at 1070 ◦C constant temperature. |
URI: | http://www.repositorio.ufop.br/handle/123456789/11468 |
DOI: | https://doi.org/10.1016/j.jmrt.2017.12.002 |
ISSN: | 2238-7854 |
Licença: | This is an open access article under the CC BY-NC-ND license (http://creativecommons.org/licenses/by-nc-nd/4.0/). Fonte: o próprio artigo. |
Aparece nas coleções: | DEFIS - Artigos publicados em periódicos |
Arquivos associados a este item:
Arquivo | Descrição | Tamanho | Formato | |
---|---|---|---|---|
ARTIGO_SecondaryRecrystallizationCharacteristics.pdf | 1,31 MB | Adobe PDF | Visualizar/Abrir |
Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.