Título: | Caracterização de uma tipologia de minério de manganês do Brasil. |
Título(s) alternativo(s): | Caracterization of a Brazilian manganese ore typology. |
Autor(es): | Reis, Érica Linhares Faria, Geraldo Lúcio de Araújo, Fernando Gabriel da Silva Tenório, Jorge Alberto Soares Vieira, Cláudio Batista Jannotti Júnior, Nelson |
Palavras-chave: | Minério de manganês Decomposição térmica Caracterização tipológica Typological characterization Thermal decomposition |
Data do documento: | 2010 |
Referência: | REIS, E. L. et al. Caracterização de uma tipologia de minério de manganês do Brasil. REM: Revista Escola de Minas, v. 63, n. 3, p. 517-521, jul./set. 2010. Disponível em: <http://www.scielo.br/pdf/rem/v63n3/v63n3a14.pdf>. Acesso em: 26 set. 2012. |
Resumo: | Visando a melhorias no benefi ciamento e no processo de fabricação de ferroligas de manganês, foi realizada a caracterização de uma tipologia predominante de minério de manganês, de ocorrência na região de Carajás, PA, BR. Obteve-se uma amostra representativa da tipologia e foram realizadas análise granulométrica por peneiramento e análise química, por ICP-AES. Foram identifi cadas por difratometria de raios X as fases minerais majoritárias. Um estudo termogravimétrico foi desenvolvido para verifi car a estabilidade térmica, ao ar, das fases minerais majoritárias. Observou-se que 19,3% da amostra encontram-se abaixo de 6,3mm. O teor de manganês no minério foi de 52,63% em peso, com 1,92% de sílica, 0,17% de fósforo e 3,13% de ferro. Foram identifi cados, na amostra, os óxidos de manganês criptomelana, todorokita e pirolusita, com goethita, quartzo, gibbisita e caolinita compondo a ganga. Para a amostra estudada, observou-se a decomposição térmica dos óxidos criptomelana e pirolusita, em torno de 600oC, ao ar. Em torno de 950oC, teve início a transformação de Mn2O3 em Mn3O4. |
Resumo em outra língua: | In order to improve manganese-iron alloy production processes, an important Brazilian manganese ore typology, placed in Carajás, PA, was characterized. A representative sample was obtained from mine. The particle size determination was performed by screening, followed by chemical analysis using plasma spectrometry (ICP-AES). The physical properties studied included density, surface area and porosity measurements (BET). The mineral constituents was identifi ed and quantifi ed by X-ray diffraction. A termogravimetrical study was done in order to verify the thermal stability of major mineral constituents in the air. It was observed that 19.3% of studied typology was below 6.3mm. The manganese, silica and phosphorus contents were 52.63%, 1.92% and 0.17%, respectively. The oxides identifi ed were cryptomelane, todorokite and pyrolusite. The other constituents were goethite, quartz, gibbsite, and kaolinite. According to the thermal study, the cryptomelane and pyrolusite start their decomposition in the air, at approximately 600°C. At around 950°C, Mn2O3 decomposition and Mn3O4 growth were observed. |
URI: | http://www.repositorio.ufop.br/handle/123456789/1428 |
ISSN: | 03704467 |
Licença: | A REM - Revista Escola de Minas - autoriza o depósito de cópia de artigos dos professores e alunos da UFOP no Repositório Institucional da UFOP. Licença concedida mediante preenchimento de formulário online em: 12 set. 2013. |
Aparece nas coleções: | DEMET - Artigos publicados em periódicos |
Arquivos associados a este item:
Arquivo | Descrição | Tamanho | Formato | |
---|---|---|---|---|
ARTIGO_CaracterizaçãoTipologiaMinério.pdf | 206,76 kB | Adobe PDF | Visualizar/Abrir |
Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.